Gas Welding Wire

Manganese Bronze

Bare & Flux Coated Welding Rod

AS 1167.1-1993 RCuZn-C

  Applications

For bronze welding of cast iron, malleable iron and steel.

  Usage Specifications

Maganese Bronze has a melting point of 890'C. It has a blue tip for easy identification and is suitable for Oxy-Acetylene welding. Available in Flux Coated or bare rod.

  Typical Composition (%)

Copper

Nickel

Silicon

Manganese

Tin

Iron

Zinc

58

~

0.1

0.1

1.0

0.5

40.3

 Typical Mechanical Properties

Tensile Strength Mpa

0.2% Proof Stress Mpa

Elongation %

Hardness Hv

460

170

35

135

 Product Information

Code

Rod Size

Flux Coated

Rod Length

Pack Size

GMB16

1.6mm

~

900mm

5.0 Kg

GMB24

2.4mm

~

900mm

5.0 Kg

GMB32

3.2mm

~

900mm

5.0 Kg

GMBFC24

2.4mm

Yes

900mm

5.0 Kg

GMBFC32

3.2mm

Yes

900mm

5.0 Kg

Tobin Bronze

Bare & Flux Coated Welding Rod

AS 1167.1-1993 RCuZn-A

  Applications

For bronze welding of brass, bronze and low strength steel joints. Not suitable for cast iron.

  Usage Specifications

Maganese Bronze has a melting point of 900'C. It has a white tip for easy identification and is suitable for Oxy-Acetylene welding. Available in flux or bare rod.

  Typical Composition (%)

Copper

Nickel

Silicon

Manganese

Tin

Iron

Zinc

62

~

0.3

~

0.5

~

37.2

 Typical Mechanical Properties

Tensile Strength Mpa

0.2% Proof Stress Mpa

Elongation %

Hardness Hv

400

110

45

130

 Product Information

Code

Rod Size

Flux Coated

Rod Length

Pack Size

GTB16

1.6mm

~

900mm

5.0 Kg

GTB24

2.4mm

~

900mm

5.0 Kg

GTB32

3.2mm

~

900mm

5.0 Kg

GTBFC24

2.4mm

Yes

900mm

5.0 Kg

GTBFC32

3.2mm

Yes

900mm

5.0 Kg

Nickel Bronze

Bare & Flux Coated Welding Rod

AS 1167.1-1993 RCuZn-D

  Applications

For high strength gas welding of ferrous metals.

  Usage Specifications

Nickel Bronze has a melting point of 910'C. It has a crimson tip for easy identification and is suitable for Oxy-Acetylene welding of nickel alloys. The weld metal has excellent wear resistance and is similar in color to the parent metal.

  Typical Composition (%)

Copper

Nickel

Silicon

Manganese

Tin

Iron

Zinc

46.5

10.0

0.2

~

~

~

43.3

 Typical Mechanical Properties

Tensile Strength Mpa

0.2% Proof Stress Mpa

Elongation %

Hardness Hv

555

250

18

170

 Product Information

Code

Rod Size

Flux Coated

Rod Length

Pack Size

GNB16

1.6mm

~

900mm

5.0 Kg

GNB24

2.4mm

~

900mm

5.0 Kg

GNB32

3.2mm

~

900mm

5.0 Kg

GNBFC16

1.6mm

Yes

900mm

5.0 Kg

GNBFC24

2.4mm

Yes

900mm

5.0 Kg

GNBFC32

3.2mm

Yes

900mm

5.0 Kg