Flux Cored Wire
|
|
|
|
SF-71
|
|
|
|
AWS A5.20 / ASME SFA5.20 E71T-1
|
|
|
|
JIS Z3313 YFW-C50DR
|
|
|
|
Applications
|
|
|
All position welding of building, shipbuilding, bridges, machinery and vehicles.
|
|
|
Usage Specifications
|
|
|
SF-71 is a titania type of flux cored wire foll all position welding with CO2. Spatter loss is low & bead appearance is good. The arc is soft with good stability & the slag covering is uniform with good removal quality’s.
|
|
|
Welding Position Welding Current Shielding Gas
|
 |
|
|
Use 100% C02 Gas Only
|
|
|
Proper preheating (50~150’C) and interpass temperature must be used in order to release hydrogen which may cause cracking in the weld metal when welding medium to heavy plates.
|
|
DC+
|
|
|
|
|
One-sided welding defects such as hot cracking may occur if the welding speed is to high.
|
|
|
|
Typical Chemical Composition Of All-Weld Metal (%)
|
|
C
|
Si
|
Mn
|
P
|
S
|
|
0.04
|
0.49
|
1.29
|
0.010
|
0.009
|
|
|
|
|
Typical Mechanical Properties of All-Weld Metal
|
|
Y.S N/mm sq
|
T.S N/mm sq
|
E.L ( % )
|
Temp 'C
|
Impact Test-J cvn
|
|
548
|
582
|
28
|
0
|
86
|
|
|
Available Size, Code, Recommended Current
|
|
Code
|
Size
|
Current Range
|
Pack Size
|
|
SF7112
|
1.2mm
|
120 ~ 300 amps
|
15 Kg
|
|
SF7116
|
1.6mm
|
180 ~ 450 amps
|
15 Kg
|
|
|
|
Supercored 71
|
|
|
|
AWS A5.20 / ASME SFA5.20 E71T-1
|
|
|
|
JIS Z3313 YFW-C502R
|
|
|
|
Applications
|
|
|
All position welding of machinery, shipbuilding, bridges. With high Impact Values of the weld metal.
|
|
|
Usage Specifications
|
|
|
Supercored 71 is a flux cored wire which has been designed to run over a wide range of positions and currents. It has a smooth and quiet arc and it’s slag detachability is good.
|
|
|
Welding Position Welding Current Shielding Gas
|
|
|
|
Use 100% C02 Gas Only
|
|
|
|
Proper preheating (50~150’C) and interpass temperature must be used in order to release hydrogen which may cause cracking in the weld metal when welding medium to heavy plates.
|
|
|
DC+
|
|
|
|
|
|
One-sided welding defects such as hot cracking may occur if the welding speed is to high.
|
|
|
|
|
Typical Chemical Composition Of All-Weld Metal (%)
|
|
C
|
Si
|
Mn
|
P
|
S
|
|
0.03
|
0.51
|
1.26
|
0.010
|
0.011
|
|
|
|
Typical Mechanical Properties of All-Weld Metal
|
|
Y.S N/mm sq
|
T.S N/mm sq
|
E.L ( % )
|
Temp 'C
|
Impact Test-J cvn
|
|
545
|
572
|
28
|
0 / -20
|
160
|
|
|
Available Size, Code, Recommended Current
|
|
Code
|
Size
|
Current Range
|
Pack Size
|
|
SC7112
|
1.2mm
|
120 ~ 300 amps
|
15 Kg
|
|
SC7116
|
1.6mm
|
180 ~ 400 amps
|
15 Kg
|
|
|
|
Supercored 70NS
|
|
|
|
AWS A5.18 / ASME SFA5.18 E70C-6M
|
|
|
|
JIS Z3213 YFW-A50DM
|
|
|
|
Applications
|
|
|
Supercored 70NS is designed to be used for shipbuilding, machinery, bridge construction, structural fabrication, automated or robotic welding.
|
|
|
Usage Specifications
|
|
|
SC70NS is a metal cored wire which combines the high deposition rates of F.C.W with the high efficiencies of a solid wire. It has a exceptionally smooth and stable ARC, low spatter and minimal slag coverage.
|
|
|
Welding Position Welding Current Shielding Gas
|
|
|
Use Argon +20~25% C02 Gas
|
|
 |
|
|
|
|
Proper preheating (50~150’C) and interpass temperature must be used in order to release hydrogen which may cause cracking in the weld metal when welding medium to heavy plates.
|
|
|
DC+
|
|
|
|
|
|
|
One-sided welding defects such as hot cracking may occur if the welding speed is to high.
|
|
|
|
|
|
|
|
Typical Chemical Composition Of All-Weld Metal (%)
|
|
C
|
Si
|
Mn
|
P
|
S
|
|
0.03
|
0.55
|
1.40
|
0.011
|
0.017
|
|
|
|
Typical Mechanical Properties of All-Weld Metal
|
|
Y.S N/mm sq
|
T.S N/mm sq
|
E.L ( % )
|
Temp 'C
|
Impact Test-J cvn
|
|
440
|
519
|
27
|
-30
|
50
|
|
|
Available Size, Code, Recommended Current
|
|
Code
|
Size
|
Current Range
|
Pack Size
|
|
SC70NS12
|
1.2mm
|
230 ~ 300 amps
|
15 Kg
|
|
SC70NS16
|
1.6mm
|
290 ~ 360 amps
|
15 Kg
|
|
|
|
SF-70MX
|
|
|
|
AWS A5.20 / ASME SFA5.20 E70T-1
|
|
|
|
JIS Z3313 YFW-C50DM
|
|
|
|
Applications
|
|
|
SF-70MX is a metal cored wire which is designed for high productive welding of structural steels in excess of 6mm.
|
|
|
Usage Specifications
|
|
|
This wire benefits from a high deposition rate with very low spatter loss. It has excellent penetration and a good stable ARC.
|
|
|
Welding Position Welding Current Shielding Gas
|
|
|
Use Argon +20~25% C02 Gas
|
|
|
|
|
|
|
Proper preheating (50~150’C) and interpass temperature must be used in order to release hydrogen which may cause cracking in the weld metal when welding medium to heavy plates.
|
|
|
DC+
|
|
|
|
|
|
|
One-sided welding defects such as hot cracking may occur if the welding speed is to high.
|
|
|
|
|
|
|
|
Typical Chemical Composition Of All-Weld Metal (%)
|
|
C
|
Si
|
Mn
|
P
|
S
|
|
0.05
|
0.50
|
1.50
|
0.011
|
0.013
|
|
|
|
Typical Mechanical Properties of All-Weld Metal
|
|
Y.S N/mm sq
|
T.S N/mm sq
|
E.L ( % )
|
Temp 'C
|
Impact Test-J cvn
|
|
560
|
590
|
28
|
0
|
60
|
|
|
Available Size, Code, Recommended Current
|
|
Code
|
Size
|
Current Range
|
Pack Size
|
|
SF70MX12
|
1.2mm
|
250 ~ 300 amps
|
15 Kg
|
|
SF70MX16
|
1.6mm
|
300 ~ 350 amps
|
15 Kg
|
|
|
|
Supercored 81-K2
|
|
|
|
AWS A5.29 / ASME SFA5.29 E81T1-K2
|
|
|
|
JIS Z3313 YFL-C506R
|
|
|
|
Applications
|
|
|
Supercored 81-K2 is used for the welding of low temperature service steels in the construction of LPG & LNG storage tanks.
|
|
|
Usage Specifications
|
|
|
Sc81-K2 is a titania type flux cored wire designed for all position welding.
|
|
|
Welding Position Welding Current Shielding Gas
|
|
|
|
Use 100% C02 Gas Only
|
|
|
|
Proper preheating (50~150’C) and interpass temperature must be used in order to release hydrogen which may cause cracking in the weld metal when welding medium to heavy plates.
|
|
|
DC+
|
|
|
|
|
|
One-sided welding defects such as hot cracking may occur if the welding speed is to high.
|
|
|
|
|
Typical Chemical Composition Of All-Weld Metal (%)
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni
|
|
0.04
|
0.35
|
1.35
|
0.012
|
0.011
|
1.50
|
|
|
Typical Mechanical Properties of All-Weld Metal
|
|
Y.S N/mm sq
|
T.S N/mm sq
|
E.L ( % )
|
Temp 'C
|
Impact Test-J cvn
|
|
540
|
620
|
28
|
-30 ~ -60
|
110
|
|
|
Available Size, Code, Recommended Current
|
|
Code
|
Size
|
Current Range
|
Pack Size
|
|
SC81K212
|
1.2mm
|
170 ~ 300 amps
|
15 Kg
|
|
SC81K216
|
1.6mm
|
200 ~ 350 amps
|
15 Kg
|
|
|
|
|
|
|
|